PRIMER SC 210

DEFINITION

Multi-purpose epoxy primer with two components, low solvent.

Public Works Pos. No: 04.379/H02

USAGE AREAS

It is used on factory and warehouse floors, working areas, loading zones, industrial floors exposed to medium and heavy loads, concrete surfaces, cement mortars and screed surfaces, normal and highly absorbent surfaces, for filling fine pores and cracks and capillary spaces on epoxy based mortars or prior to application of epoxy, polyurethane, polyurea topcoats,

Type

TS EN 1504-2/ April 2008 Principle 5(PR): 5.1 Physical Resistance / Surface Improvement Coating Application ©

Colour

Colourless

Outlook

Mat

Solid Matter by Weight, %

85

Density

1,06 gr/cm³

Waste

0,300 – 0,500 kg / m2

Package

12,50 kg A  Component + 5 kg B Component : Total 17,50 kg

Flash Point

>25 °C

Mixture Ratio

2,5 / 1

Application Methods

Brush, Roller, Trowell, Air Gun, Airless Gun

Mixture Life

60 min / 25°C

Shelf Life

1 year

Waiting Time Between Coats

12 hours / 25°C

Drying Time

12 hours / 25°C

Mechanical Strength

7 days

Equipment Cleaning

Epoxy Thinner

SURFACE PREPARATION
Free particles and paint residues on the surface must be thoroughly cleaned, brokens and cracks must be repaired, surfaces should be roughened mechanically (blastrack or milling router) and cleaned from vacuum with vacuum cleaner

MIXING PREPARATION
A and B component should be mixed with a low speed mixer for at least 3-4 minutes until a homogenous mixture is obtained by paying attention to mixture ratios. It is ready for application after mixing.

APPLICATION CONDITIONS

* Surface should have sufficient strength. The concrete should have a compressive strength of at least 25 N/mm² and a tensile strength of at least 1,5 N/mm².

* Surfaces must be clean, smooth and dry. Humid is not pass 5%. If the humidity is above this ratio, SC 220 Epoxy Prime for Humid Surfaces should be preferred.

* SC 210 multipurpose epoxy prime should be completed its curing before the top coat coating is started.

* Avoid application in very humid environments and below 10°C.

* Mixing ratios should be considered. Products that can be used upper this product:

* SC 650 ST Solvent Free Epoxy Resin Based Top Coat Coating

* SC 605 Epoxy Top Coat Paint for Vertical Surfaces

* SC 645 Orange Coat Patterned Top Coat Epoxy Coating

* SC 902 Solvent Free Epoxy Top Coat Coating

* SC 905 Solvent Free Epoxy Paint Resistant to Chemical Matter for Vertical Surfaces

* SC 950 Solvent Free Epoxy Coating Resistant to Chemical Matter

* PU 145 Polyurethane Self Leveling Coating

* PU 150 Polyurethane Semi-Elastic Self Leveling Coating

* PU 160 Polyurethane Elastic Water Isolation Membrane

* PU 170 Polyurethane Water Isolation Membrane